UPVC low wave roof sheet  T900

UPVC low wave roof sheet T900

Model
T900
Color
White, Blue, Green,Yellow, Red, Dark Green, or Customized
Length
Customized
Package
Nude / Customized
Minimum Order
1000 Sqms
Delivery Time
1 x 20'/40'container 10 Days
Price Term
FOB or CNF
Payment Terms
T/T or L/C at sight
Application
factory roof, warehouse roof, wall panel etc.
Price
Get Latest Price
Get the latest price
Quantity Needed:
Pieces
E-mail:
Brand: Xingfa
Model: T900
Width: 900mm
Efficient width: 840mm
Thickness: 1.5mm,2.0mm,2.5mm,3.0mm
Length: Customized (20'container 5.8 meter, 40'container 11.8 meter)
Purlin distance: 660mm-880mm
Surface finishing: ASA coated,Embossed type,standard type.
Color: White, Blue, Green, Yellow, Red, Dark Green, or Customized
◇◆ Product Description

UPVC low wave roof sheet


It is made of main raw material of PVC resin supplemented with anti-UV additive ,and made by scientific formula and unique process technology. It is occupied with good fire resistance,weather resistance and electrical insulation,which is an excellent anti-corrosion material. Provide the quality guarantee for 10 years.


T900 Specification

Model

 T900

Width

 900mm

Efficient width

 840mm

Thickness

 1.5mm,2.0mm,2.5mm,3.0mm

Length

 Customized (20'container 5.8 meter, 40'container 11.8 meter)

Applications

 factory roof, warehouse roof, wall panel etc...

Surface finishing

 ASA coated,Embossed type,standard type.

Layer

 Single layer, Three layers, Four layers


T1130 Specification

Model

 T1130

Width

 1130mm

Efficient width

 1050mm

Thickness

 1.5mm,2.0mm,2.5mm,3.0mm

Length

 Customized (20'container 5.8 meter, 40'container 11.8 meter)

Applications

 factory roof, warehouse roof, wall panel etc...

Surface finishing

 ASA coated,Embossed type,standard type.

Layer

 Single layer, Three layers, Four layers


T1350 Specification

Model

 T1350

Width

 1350mm

Efficient width

 1260mm

Thickness

 1.5mm,2.0mm,2.5mm,3.0mm

Length

 Customized (20'container 5.8 meter, 40'container 11.8 meter)

Applications

 factory roof, warehouse roof, wall panel etc...

Surface finishing

 ASA coated,Embossed type,standard type.

Layer

 Single layer, Three layers, Four layers


T1360 Specification

Model

 T1360

Width

 1360mm

Efficient width

 1260mm

Thickness

 1.5mm,2.0mm,2.5mm,3.0mm

Length

 Customized (20'container 5.8 meter, 40'container 11.8 meter)

Applications

 factory roof, warehouse roof, wall panel etc...

Surface finishing

 ASA coated,Embossed type,standard type.

Layer

 Single layer, Three layers, Four layers

◇◆ Product Feature
  •  

    Fireproof

  •  

    Acid and alkali resistance

  •  

    Toughness

  •  

    Weather resistance

  •  

    Low noise

  •  

    Portability

  •  

    Environmental protection


undefined
undefined


◇◆ Product Details
undefined
                   
pvc wall sheet
                   
++
                   
roof tile in plastic
                   
++
undefined
undefined
                   
three layer upvc roof sheet
                   
++
                   
upvc roofing
                   
++
undefined
undefined
                   
upvc sheet
                   
++


◇◆ Product Size & Color


undefined

900 size


undefined

1130 size


undefined

1350 size


undefined

1360 size

undefined

UPVC roof color


◇◆ Test Report

UPVC TEST REPORT


Num.

Test item

Test method

The test condition

Test result

1

Tensile strength

ISO 527-1:2012 & ISO 527 -2:2012

Testing speed: 50mm/min

23.1 Mpa

2

Flexural strength

ISO 178:2010/Amd.1:2013 Method A

Test speed: 1mm/min

50.9 Mpa

3

Impact Resistance

With reference to GB/T 8814-2004 Section 5.7, Section 6.7 and client’s requirement

-10°C, 1h
     Strike weight:1000g
     Height:1000mm

Number of specimen failures: 0

4

Vicat Softening Temperature

ISO 306:2013 Method B 50

Rate of temperature: 50K/h

77.0°C

5

Effects of liquid chemicals

ISO 175:2010

Temperature: 23°C
     Immersion time:48h
     40%(m/m) NaOH

No visual change

ISO 175:2010

Temperature: 23°C
     Immersion time:48h
     35%(m/m) HCl

Visual discoloring, but no other visual change

ISO 175:2010

Temperature: 23°C
     Immersion time:48h
     30%(m/m)H2SO4

No visual change

6

Light Ageing Test – Xenon-arc Exposure

ISO 4892-2:2013 cycle 4 & ISO 105-A02:1993/Cor.2:2005 & ASTM D2244– 15a

Exposure period: 1000h

Grey scale: 3
     △E*ab : 1.3

7

Dimensional Stability

With reference to ASTM D1204-14 and client’s requirement

100℃,60min→23±2℃, 50±5% RH, 60min

Direction of arrow: -0.6%
     Perpendicular to Direction of arrow: 1.6%


NO.

Test item

Test method

Test condition

Result

1

Tensile strength

ASTM D638-03

Specimen: Type I
     Speed: 50mm/min

Before aging

29.2 MPa

After aging

36.9MPa

2

Flexural strength

ASTM D790-07 Procedure A and client’s requirement

127x13.07x1.98mm
     Speed: 0.8mm/min
     Span: 30mm

Before aging

59.3MPa

After aging

62.8MPa

3

Thermal Conductivity [W/(m·K)]

ASTM C518-04

----

0.08846

4

Coeffcient of Linear Thermal Expansion(μm/m·℃)

Rf.ASTM D696-03

---

49.68

5

Vertical Burning

UL 94-1996REV.9:2006 section 8

Specimen: 129x12.9x1.99mm

V-0

6

Oxygen Index

ASTM D2863-06a

Specimen:Type III
     Thickness: 1.97mm
     Ignition prceduce: Method A

36.3%

7

Water absorption

ASTM D570-98(2005)

Drying :50℃,24h
     Immersion: 23℃,24h

0.04%

8

 Vicat softening temperature

ASTM D1525-06

Thickness: 3.92mm
     2pcs plied up
     Rate of temperature rise: 50℃/h
     Load: 1.82MPa

90.0℃

9

Heat deflection temperature

ASTM D648-07 Method B

Width: 12.83mm
     Depth: 3.73mm
     Heating rate: 120℃/h
     Load:1.82MPa

55.6℃

10

High temperature

Supplied by client

60℃,6h

No visible change

11

Impact resistance (Gardner impact)

ASTM D5420-04

Statement of geometry: GE(striker:φ16.26mm)
     Thickness:2.00mm

Mean-failure energy 6J

12

Low temperature resistance

Supplied by client

-35℃,6h

No visible change

13

Chemical resistance

Supplied by client

70% Ethanol Solution, (m/m),23℃,2h

No visible change

10% NaOH Solution, (m/m),23℃,2h

No visible change

Saturation NaCI Solution 23℃,2h

No visible change

14

UV Exposure

ASTM G154-06 Cycle 1,ISO 105-A02:1993

8h UV at(60±3)℃ BPT, 0.89W/(m2·nm)@340nm 4h condensation at (50±3)℃ BPT Exposure period:1000h

Grey scale: 3


◇◆ Product Applications


undefined
UPVC low wave roof tile project show 1
undefined
UPVC low wave roof tile project show 2


◇◆ Company Strength


About our Company

 
With more than 15 years`s experience in Plastic Roof Sheet industry, Xingfa has been focusing on product research and development. Now we have over 10 production lines,production capacity over 800,000 sqms per month, becoming the most professional manufacturer of PVC Roof Sheet in the world. It owns senior expert-level R&D team and advanced equipment, unique processes and strict management. Our company have good software and hardware facilities and it has pass ISO 9001:2008 International Quality System Certification.
undefined        



Product Message
社媒暂无评论
Chat Online 编辑模式下无法使用
Chat Online inputting...